NOELSON™ SFPP-600M/SFPP-800M, Compound Ferro-titanium Pigment (Ace Shield Pigment L-B/L-C)
Start formulation
Epoxy zinc rich coating:
| Part A | ||
| Epoxy resin | 23 | 60% in xylene |
| Bentone | 1 | CLAYTONE HY/HT By Noelson Chem |
| Zinc dust | 54 | 325 Mesh |
| Ferro-phosphorous Powder | 10 | NOELSON™ SFPP-800M, can also be replaced full or in part by Compound Ferro-titanium Powder (Ace Shield Pigment L-B/L-C) |
| TiO2 | ||
| Sericite mica | 2 | |
| Wollastonite | 3 | |
| Mixed solvent | 9 | |
| Part B | ||
| Epoxy resin hardener | 100 | |
| A/B= 10/ 1 (by weight) | ||
Water-based zinc rich primer:
| Part A | ||
| High modulus lithium silicate | 20-30 | |
|
Standard modulus lithium silicate |
50-70 | |
| Part B | ||
| Bentone | 5-10 | CLAYTONE HY/HT By NoelsonChem |
| Plasticizer | 30-40 | |
| Zinc dust | 100-150 | 325 Mesh |
| Ferro-phosphorous Powder | 40-50 | NOELSON™ SFPP-800M, can also be replaced full or in part by Compound Ferro-titanium Powder (Ace Shield Pigment L-B/L-C) |
| A/B= 2.5/ 1 (by weight) | ||
Notice: Switching dosage of Zinc & SFPP is constraint by cost.
Epoxy-polyamide zinc-rich primer:
| Part A | ||
| Epoxy resin | 3.66 | |
| Mixed solvents | 10.92 | |
| Anti-settling agents | 0.78 | |
| Wetting agent | 0.32 | |
| Drying agent | 0.66 | |
| Zinc phosphate | 3.5 | NOELSON™ ZP 409-1 |
| Ferro-phosphorous Powder | 19 | NOELSON™ SFPP-800M |
| Zinc dust | 57.2 | |
| Part B | ||
| Polyamide resin | 1.96 | |
| Mixed solvents | 2 | |
| A/B = 96.04:3.96 (by weight) | ||